| HOOK-UP WIRE | UL 1672 | ||||
 |
Product Construction 產(chǎn)品結(jié)構(gòu) | ||||
| Conductor 導(dǎo)體 |
Material 材料 | Tinned Copper 鍍錫銅絲 | |||
| AWG 線規(guī) | 18 | ||||
| Conductors No 導(dǎo)體數(shù) | 41 | ||||
| Diameter 規(guī)格(mm) | 0.16 | ||||
| Jacket 護(hù)套 |
Material 材料 | PVC | |||
| Average Thickness 平均厚度(mm) | 0.82 | ||||
| Minimun Thickness 最小厚度(mm) | 0.74 | ||||
| Diameter 線徑(mm) | 2.80 | ||||
| Product Standard 產(chǎn)品標(biāo)準(zhǔn) | |||||
| Rated Temperature 額定溫度（℃） |
105 | ||||
| Rated Voltage 額定電壓（V） |
600 | ||||
| Product Standard Certification | E308941 | ||||
| Passes UL VW-1 & CSA FT1 vertical flame test 通過(guò)UL VW-1 & CSA FT1垂直耐燒測(cè)試 |
|||||
| Reference Standard | UL 758 UL 1581 | ||||
| Printing 印字 | |||||
AMCOWRE E308941  AWM STYLE 1672 18AWG 105℃ 600V VW-1 --- c AWM 1 A/B 105℃ 600V FT1 -F- -LF- ROHS S&Y |
|||||
| Mechanical Characteristic 物理機(jī)械性能 | |||||
| Testing Object 檢測(cè)對(duì)象 | Jacket Material 護(hù)套料 | ||||
| Testing Material 實(shí)驗(yàn)材料 | PVC | ||||
| Aging Condition 老化條件（℃*hrs） | 136*168 | ||||
| Befor Aging 老化前 |
Tensile Strength 抗張強(qiáng)度（Mpa） | >=10.35 | |||
| Elongation伸長(zhǎng)率(%) | >=100 | ||||
| After Aging 老化后 |
Tensile Strength 抗張強(qiáng)度(Mpa) | >=70% of unaged | |||
| Elongation伸長(zhǎng)率(%) | >=65% of unaged | ||||
| AWG 線規(guī) |
Conductor No./mm 導(dǎo)體數(shù)/線徑（mm） |
Jacket Diameter 護(hù)套線徑（mm） |
Jacket Average Thickness 平均厚度（mm） |
Jacket Minimum Thickness 最小厚度（mm） |
Weight 重量 |
| 16 | 26/0.254 | 3.12 | 0.41 | 0.41 | 21.30 |
| 18 | 41/0.16 | 2.80 | 0.41 | 0.41 | 15.41 |
| 20 | 26/0.16 | 2.56 | 0.41 | 0.41 | 11.67 |
| 22 | 17/0.16 | 2.22 | 0.41 | 0.41 | 8.64 |
| 24 | 11/0.16 | 2.10 | 0.41 | 0.41 | 7.06 |
| 26 | 7/0.16 | 2.00 | 0.41 | 0.41 | 5.93 |
| 28 | 7/0.127 | 1.92 | 0.41 | 0.41 | 5.13 |